Retarded gypsum plaster for use in long set aggregated mortar applications

ABSTRACT

The process of making a gypsum plaster possessing a high degree of stability over extended periods of time and having a set time of at least 4 hours in aggregated mortar applications by providing a specially sized calcined gypsum having a particle size that is essentially all finer than 32 microns, and mixing said specially sized gypsum with retarder, accelerator and other additives to give the desired properties when mixed with water and aggregate.

United States Patent Lane [54] RETARDED GYPSUM PLASTER FOR USE IN LONG SET AGGREGATED MORTAR APPLICATIONS [72] Inventor: Marvin K. Lane, Chicago, ill.

1 73] Assignee: United States Gypsum Company, Chicago,

Ill.

[22] Filed: Apr. 1, 1969 [21] Appl.No.: 812,371

s21-u.s.c| ..l06/110 511 mu. ....C04b 11/00 [58] FieldoiSearch nos/110415;

[451 Mar. 28, 1972 [56] References Cited UNITED STATES PATENTS 3,328,121 6/1967 Shull ..106/110 3,445,323 5/1969 Schnabel 106/ l 10 Primary Examiner-James E. Poer Attorney-John Kenneth Wise [5 7] ABSTRACT The process of making a gypsum plaster possessing a high 1 Claims, No Drawings RETARDED GYPSUM PLASTER FOR USE IN LONG SET AGGREGATED MORTAR APPLICATIONS This invention relates to the preparation of a gypsum plaster exhibiting increased resistance to aging during storage by using a specially sized calcined gypsum plaster that is essentially free of plus-32-micron particles.

Currently manufactured retarded and formulated gypsum plaster made by atmospheric calcination has a rather high mortar consistency when used with an aggregate such as sand or perlite. When aggregated mortar pastes made from this gypsum plaster are awaiting application by hand or by pumping through a machine, they manifest severe stiffening, making it very difficult to control and predict the set, dried density after application. Furthermore, the mortar consistency of this gypsum plaster drops with are during storage for long periods of time. The aggregated mortar paste made from this aged gypsum plaster becomes lean, dead, sandy and sticky, and it has poor working qualities and poor sand-coating and sandcarrying ability under a trowel.

Current gypsum plaster made by atmospheric calcination contains about 40 percent by-weight of particles larger than 32 microns. l have discovered that by size-classifying the gypsum plaster to produce a specially sized gypsum plaster having percent to percent by-weight of particles larger than 32 microns, the plaster will give a lower mortar consistency, will manifest only very slight stiffening, will drop only very slightly in mortar consistency with aging and will not develop poor working qualities and poor sand-coating and sand-carrying ability with aging during long periods of storage.

Atmospherically calcined gypsum hemihydrate is used in long-set, aggregated mortar mixes that are applied and formed either by hand trowel or by a machine spray device and allowed to set and dry. Generally, these are the basecoat type applications, but this invention is not limited thereto.

Calcined gypsum hemihydrate intended for this use is formulated with proteinaceous retarder, some type of accelerator as a set stabilizer and other miscellaneous ingredients added to impart specified properties and then bagged, shipped and stored. This type of bagged, formulated, calcined gypsum hemihydrate is commonly known in the industry as gypsum plaster or machine applied gypsum plaster and it gives about a 4 to 6 hour set in an aggregated mortar mix. At a later date, the gypsum plaster is mixed with water and aggregate and is applied. The aggregate is generally sand or perlite and the ratio of aggregate to gypsum plaster in the mortar mix with water is between 2:1 and 4:1 depending on the application. This mix is stirred by hand or by machine and brought to a pastelike fluidity by incremental additions of water. An aggregated mortar paste fluidity is defined by ASTM test procedure No. C-472-6l using the Modified Vicat plunger and a penetration of 20 mind-.3 min. This aggregated mortar paste is then gradually applied by hand during a period of about an hour or more; or it is applied through a pump, long hose and spray device.

In the case of hand application, an aggregated mortar slurry will tend to buck as it is called in the trade. This refers to a stiffening, or thickening, of the paste during standing while it is being applied with a hod and trowel. When this occurs, it is necessary to add water to bring the fluidity back to the desired mortar consistency so that it can still be applied smoothly and easily. in the case of machine spray application, these aggregated mortar slurries stiffen very rapidly as they pass through the hose and, if the change in fluidity is very large, it is very difficult to maintain control and to spray smoothly.

Another drawback of gypsum plaster is its susceptibility to aging during storage. This aging is magnified and accelerated by a humid environment. Aging consists of two changes: first, the gypsum plaster develops a lower mortar consistency and, second, it becomes poor-working, lean, and sticky under a trowel, and it is no longer able to coat and carry very coarse sand particles. If this aged material is machine-applied, the sand separates in the hose, and this results in plugging.

it would be advantageous for an aggregated mortar mix made from fresh gypsum plaster to have a lower mortar consistency.

Furthermore, it would be advantageous if the aggregated mortar fluidity, once measured, could be maintained constant during application; i.e., the mortar would not stifien or buck."

It would also be advantageous if the fresh gypsum plaster maintained a constant mortar consistency during storage in bags prior to use. Also, it would be advantageous if it maintained its richness and trowelability and sand-coating and sand-carrying ability during storage.

It is an object of this invention, therefore, to provide a fresh formulated, retarded gypsum plaster that has a lower mortar consistency when mixed with two to four parts of aggregate per part of plaster, as measured by the Modified Vicat apparatus, than heretofore possible, and still has good richness, trowelability and sand-coating and carrying ability.

A further object of this invention is to provide a fresh formulated, retarded gypsum plaster which, after it is once mixed to a mortar consistency with aggregate in readiness for hand trowel application and forming, maintains about the same fluidity throughout the period of about an hour, which is about the time required for application, without stiffening, bucking or requiring additional water.

A still further object of this invention is to provide a fresh gypsum plaster that, after mixing to a mortar consistency with aggregate, maintains a constant fluidity as it passes through a pump, hose and spray device during machine spray application and forming.

A further object of this invention is to provide a gypsum plaster that, during storage for long periods of time prior to mixing with water and aggregate for application, drops only very slightly in mortar consistency.

Another object of this invention is to provide a gypsum plaster that during storage for long periods of time prior to mixing with water and aggregate for application and forming does not develop leanness, stickiness, nor poor workability under a trowel, and does not lose sand-coating and sand-carrying ability.

It is a further object of this invention to provide all of the above described improvements by size-classifying to give an atmospherically calcined gypsum hemihydrate plaster that is essentially free of plus-32-micron particles.

This invention is based on the discovery that dry particles of freshly calcined gypsum plaster disperse" or disintegrate in water during mixing. The presence of an aggregate, such as sand or perlite, promotes this disintegration. Disintegration in the presence of an abrasive aggregate is very rapid and fully completed in a very short time, even though mixing-is mild. This disintegration phenomenon is discussed in detail, as it applies to sanded mortars, in an article published in Rock Products, March and Apr. 1968 entitled, Disintegration of Plaster Particles in Water."

The particles in plaster made by calcining atmospherically are very strained and fissured. When these particles are added to water and stirred, they break down into extremely fine fragments. The larger plaster particles (over 32 microns) are more strained and more fissured, and break down more easily and rapidly. The smaller plaster particles (below 32 microns) have more crystalline integrity and do not break down as easily. When plaster ages the strain on the larger particles diminishes and the fissures heal; as a result, these particles disintegrate to a lesser degree after aging and, if aging is severe enough, they may lose nearly all their disintegrability.

The larger particles in gypsum plaster are, therefore, quite unstable with respect to the viscosity, sand-coating ability, richness and age-stability of an aggregated mortar paste.

In order to understand and interpret the relationship between plaster particle fineness and the physical properties of the aggregated mortar slurries, the particle size of the fully disintegrated plaster must be considered as well as the particle size of the dry plaster.

The bucking or stiffening of an aggregated mortar paste is caused by the turnover from very coarse particles to very fine fragments during stirring and/or standing. The greater the extent of this turnover, or the greater the net transition in fineness, the more the paste will buck or stiffen.

"9319). as o e coats sand, in

3 The richness, trowelability, sand-coating and sand-carrying ability depends on the quantity of very fine fragments that are made available in the mortar paste by the full disintegration of I the particles. More fine fragments impart improved richness! improved trowelability and improved sandcarrying and sand-i coating ability.

However, if a mortar paste of aggregate and plaster relies on full disintegration for the fine fragments of plaster that are required, then upon aging, the mortar paste becomes very lean and dead and the sand becomes bare with no sand-carrying ability because the plaster has lost most of its disintegrability.

The objective of this invention, then, is to improve atmospherically calcined gypsum plaster by removing essentially all of these very unstable plus-32 -micron particles with' an air-classifier in a closed circuit. This will give an age-stable, rich plaster that manifests very little stiffening, has a lower mortar consistency and has good sand-carrying and sand-coating ability.

The following examples will demonstrate the effectiveness of my invention. A typical kettle calcined gypsum plaster, hav-i s about 40 p rs it-W i of anislsslmathsa 12 the standard ASTM modified Vicat apparatus and procedure, designation No. C-472-6 1. This method consists of charging a dry mix of retarded (4-hr.) plaster and sand to a measured amount of water in a stirring pan, stirring with a spatula at 60 rotations a minute, forming a patty of given dimensions and allowing the modified Vicat plunger to drop through the mortar paste from a given height. A penetration of 20 minfl min is considered to be a mortar fluidity (consistency).

Since these mortar mixes stiffen with stirring and/or standing, different degrees of stirring, other than 60 rotations, or different times of standing, will give different mortar" consistencies by this test. The test can therefore be used to measure stiffening quantitatively ,by obtaining a series of mortar" consistencies at different degrees of stirring and/or standing times on the same mix with additional increments of water. These figures are shown in Table l. y In many applications of hand-applied aggregated mortar mixes very little actual stirring is done. ThereforqTie first mortar consistency tabulated in Table l is that measured with just four or five stirs. The standard ASTM value for 80 stirs is 91 35955!- Thi imu at s mer clash sme sm TABLE 1 [Slzing, stiflening, and working property data for fresh, kettle-calcined plaster in sanded mortar] Current Specially typically sized sized Specially plaster plaster sized with 70% with plaster larger about 40% with 0% than 32 larger than larger than microns 32 microns 32 microns (l) Mortar consistency, cc. per 100 g. of plaster (with 2% parts of sand), after 4 to 5 stirs with spatula, ml APP 74 73 67 (2) ASTM mortar consistency, cc. per 100 g. of plaster (with 295 parts of sand), after 60 to 80 stirs with spatula ml- 80 73 (3) Mortar consistency, cc. per 100 g. of plaster (with 2% parts of sand), after continual vigorous stirring an replenishing with water as mix stiffens until maximum equilibrium consistency is reached, ml 110 110 38 Potential stiffening range, cc. per 100 g. of plaster, with stirring:

(3) minus (2), ml +28 +30 +15 (3) minus (1), ml +36 +37 +2 Mortar consistency, cc. per 100 g. o plaster (with 2% parts of sand), after standing for 1% hours, ml 100 90 77 Actual stiffening while standing, cc. per 100 g. of plaster (with 2% parts of sand), ml.. +26 +17 +10 Mean particle size of dry plaster, microns 24 7 Mean particle size of fully-disintegrated laster, micro 1. 1 l. 2 2. 2 Particles smaller than 1 micron in dry p aster, wt. perce 0. 5 2 5 Particles smaller than 1 micron in fully-disintegrated plaster, w 43 32 Specific blaine surface area of dry plaster, sq. cm. per g 2,000 8, 500 12,000 S ific blaine surface area of iully-disintegrated plaster, sq 30,200 30,000 000 Vdorking quality under a trowel (1) (2) a I Rich, fast soaking, coats sand, very rapid "bucking. 1 Rich, fast soaking, coats sand, rapid bucking". 1 Rich, fast soaking, coats sand, mild "bucking' microns, was size-classified at 32 microns giving a fine cut having no plus-32-micron particles and a coarse out having 70 percent plus-32-micron particles. After size classifying, the cuts each had a conventional retarder and accelerator mixed consistency prior to pumping through a long hose and spray device. The maximum mortar consistency is an equilibrium value achieved by stirring at least 1,000 rotations. Mortar consistencies will approach this value during the time the mortar therein by conventional mixing apparatus. in the following extravelirtgthrgugh a pump longhgse tnd spray d e vice periments these two cuts were compared to the typical materi- The a om ying arti l size d ta of the la ter, d a d al. fully disintegrated, are also shown in Table l. The last item in EXAMPLE 1 Table l is a description of the working quality and sand-carry- The three fresh plasters, two of special sizing and one of typ-i' "f ablhtfy i the m'xes made from the three d'fierem ical sizing, were measured for mortar consistency using 2% 19958 0 a i s. parts of 1:10. I Torpedg sand per part of plaster, by means of; Data m th 1s tables how that stiffening in a sanded mortar TABLE 2 [Sizing and aging ofkettle-calcined formulated plaster in a sanded mortar] Specially sized Current typically Specially sized plaster with sized plaster with plaster with larger than 32 about 40% larger larger than 32 morons than 32 microns microns Fresh Aged Fresh Aged Fresh Aged Mortar consistency, ml. per 100 g. of plaster, (with 2% parts of sand), after 4 to 5 stirs with spatula, ml pp. 76 65 73 65 67 63 Aging drop, ml 8 -4 A TM mortar consistency, ml. per 100 g. of plaster, (with 2% parts 0 stirs with spatula, rnl 82 68 73 68 Aging drop, ml l4 Working quality under a trowel (0 Aging chance 0; Fully-disintegrated mean particle size, microns 1. 1 30 1. 2 18 2. 2 4 Fully-disintegrated particles smaller than 1 micron, wt. (percent).. 45 2 43 5 32 28 1 Rich, fast soaking, coats sand, very rapid bucking. 1 Lean, slow soaking, sand bare, dewater.

3 Rich, iast'soaking, coats sand, rapid bucking.

4 Lean, slow soaking, sand fairly bare dewater.

bucking.

| Rich, fast soaking, coats sand, no bucking. 1 Became very dead, lean.

! Became dead lean.

F Stayed rich.

mix is related to the net transfer from very coarse particles to 7' very fine fragments during the plaster particle disintegration. The very coarse cut, containing 70 percent by weight of particles larger than 32 microns in the dry condition is the worststiffener. Typical gypsum plaster, having 40 percent by weight of particles larger than 32 microns, shows less stiffening. The

fine cut, with no plus-32-micron particles shows only slight:

EXAMPLE 2 The three samples of retarded gypsum plasters, representing different particle sizings, were aged by exposing them to 90 F 65 percent RH environment for 10 days. Then, mortar tests were repeated and side-by-side comparisons were made with the original samples that had been kept fresh by sealing them in vapor proof bags. Fully disintegrated fineness tests were run again on the aged samples. Data are shown in Table 2.

None of the three aged samples manifested stiffening because during the aging period the larger, disintegrable particles over 32 microns in size healed and lost essentially 80 percent of their ability to disintegrate in the water. In the mortar mix, therefore, there was very little fineness change from dry to disintegrated. The fineness in the mortar mixes was therefore about the same as the dry fineness, after aging.

This loss of disintegrability with aging caused the largest change in the mortar properties of the coarse sizing of plaster percent plus-32-microns by weight) and of the typical sizing of plaster 40 percent plus-32-microns by weight), because these lasters contained the largest quantity of the unstable plus-3 -m1cron particles. The fine sizing of plaster (0 percent plus-32microns by weight) changed only slightly with aging. This fine sizing of plaster was quite fine in the dry state and disintegrated slightly when it was fresh. Afler aging, it was still quite fine in the dry state and still disintegrated slightly.

The coarse sizing and typical sizing of plaster showed a large drop in mortar consistency with aging. The fine sizing of plaster maintained about the same mortar consistency with ag- The coarse sizing and typical sizing of plaster became very dead, very lean and very poor working under a trowel in a mortar mix after aging; the sand was bare and uncoated causing grittiness and stickiness after aging. The fine sizing of plaster was, however, still rich, very workable and still had good sand-coating and sand-carrying ability after aging because it still disintegrated slightly and supplied sufficient fine fragments to impart these favorable properties.

Having thus described and exemplified my invention,

I claim:

1. In a process of manufacturing a stable gypsum plaster for use in slow-set aggregated mortars, the process including the step of mixing calcined gypsum with retafder and accelerator; the improvement comprising, prior to said mixing step, the steps of size-classifying the calcined gypsum into a fine fraction containing essentially no particles larger than 32 microns and a coarse fraction containing essentially all the particles larger than 32 microns, and recovering said fine fraction for said use.

Patent No. 3, 5 ,3 9 Dated March 28, 1972 InVentor(s) 'V n K. Lane It is certified that error appears in the above-identified patent and that said Letters Patent are hereby corrected as shown below:

Column 1, line 15, "are" should read age Table 1, column 4, under "specially sized plaster with 0% larger than 32 microns", the fifth entry in that column should read plus 21 instead of "plus 2 Table 2, column 4, eachof the entries forthe two cate gories "aging drop, ml" should be entered under the heading "aged" rather than under the heading "fresh". In addition,

the category "aging chance" should read aging change The values for this entry footnoted as "7", "8 and "9" should be entered under the heading "Aged" rather than "Fresh".

Signed and sealed this 27th day of February 1973.

(SEAL) Attest Z EDWARD I I.PLETCHER,JR. ROBERT GOTTSCHALK Attestlng Officer Commissioner of Patents FORM PO-lOSO (10-69) I USCOMM-DC 60376-P69 us. GOVERNMENT PRINTING OFFICE: was o-ass-asa 